TRIEL® 5401BM BK
热塑性聚酯弹性体
Samyang Corporation
Technical Data
产品说明
• TRIEL is the registered trademark of thermoplastics polyester ester elastomer manufactured by Samyang corporation. TRIEL resins offer superior mechanical properties, elasticity, heat resistance, flexibility and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor recreation equipments.
• TRIEL is a thermoplastic polyether ester elastomer copolymer consisting of a hard segment of polybuthylene terephthalate and soft segment of polyether glycols.
CHARACTERISTICS
• Superior heat resistance
• Low temperature performance
• Workable under a wide range of temperatures
• High elastic performance
• Remarkable chemical resistance
• Good weather resistance
APPLICATIONS
• TRIEL5401BM BK grade is designed for Blow molding components.
• Automotive : Boots and bellows, ducting, airbag covers
• Industrial : tubes & hoses
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • Samyang Corporation
供货地区 • 北美洲 • 欧洲 • 亚太地区
• 高弹性 • 耐低温 • 耐热性，高
性能特点 • 共聚物 • 耐化学性良好
• 良好的柔韧性 • 耐气候影响性能良好
用途 • 吹塑成型应用 • 管道 • 汽车领域的应用：
• 电气/电子应用领域 • 管道 • 室外应用
外观 • 黑色
形式 • 颗粒料
物理性能 额定值单位制 测试方法
比重 1.15g/cm³ ASTM D792
熔流率 (230°C/2.16 kg) 1.0g/10 min ASTM D1238
收缩率 - 流动 1.6% ASTM D955
吸水率 (23°C, 24 hr) 0.45% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 ASTM D638
-- 3 23.0MPa
5.0% 应变 4.00MPa
10% 应变 6.00MPa
50% 应变 11.0MPa
伸长率 (断裂) > 400% ASTM D638
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 ASTM D256
-40°C 无断裂
23°C 无断裂
硬度 额定值单位制 测试方法
硬度计硬度 (邵氏 D) 40 ASTM D2240
热性能 额定值单位制 测试方法
热变形温度 (0.45 MPa, 未退火) 56.0°C ASTM D648
维卡软化温度 155°C ASTM D1525 4
TRIEL® 5401BM BK
热塑性聚酯弹性体
Samyang Corporation
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.59 mm) HB UL 94
注射 额定值单位制
干燥温度 100 到 110°C
干燥时间 3.0 到 4.0hr
建议的最大水分含量 0.020%
螺筒后部温度 200 到 220°C
螺筒中部温度 220 到 250°C
螺筒前部温度 220 到 250°C
射嘴温度 220 到 250°C
加工（熔体）温度 220 到 250°C
模具温度 30.0 到 50.0°C
背压 0.00 到 0.100MPa
螺杆转速 10 到 50rpm
排气孔深度 0.020 到 0.080mm
|