Keyflex® BT 1040D
热塑性聚酯弹性体
LG Chem Ltd. 

Technical Data

产品说明

KEYFLEX BT-1040D has flexibility and elastic resiliency similar to those of rubber as well as mechanical strength , heat-resistnace and weather-resistance better than those of rubber. All grade of KEYFLEX BT are block copolymers consisting of a hard(crystaline)segment of polybutylene-terephthalate and a soft(amorphous) segment based on long-chain polyether glycol.Properties are determined by the ratio of hard to soft segment.

总体

材料状态 • 已商用：当前有效   
UL 黄卡 1 •  E67171-463886
  
  •  E248280-100040718
  
     
搜索 UL 黄卡 •  LG Chem Ltd.
  
 •  Keyflex® BT
  
     
供货地区 • 北美洲 • 欧洲  
 • 南美洲 • 亚太地区  
     
性能特点 • Block Copolymer • 耐气候影响性能良好 • 耐热性中等 
用途  • 传送带修补 • 管道 • 管道 
形式  • 颗粒料   

物理性能  额定值单位制 测试方法
比重  1.16g/cm³ ASTM D792
熔流率 (200°C/2.16 kg) 20g/10 min ASTM D1238
收缩率 - 流动 0.80% ASTM D955
吸水率 (23°C, 24 hr) 0.60% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度   ASTM D638
屈服 3  5.88MPa 
5.0% 应变 2.35MPa 
弯曲模量 4 58.8MPa ASTM D790
弹性体  额定值单位制 测试方法
抗张强度 3 (断裂) 22.6MPa ASTM D412
伸长率 3 (断裂) 850% ASTM D412
撕裂强度  118kN/m ASTM D624
压缩永久变形 (70°C, 22.0 hr) 58% ASTM D395
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (-40°C) 无断裂 ASTM D256
反向缺口冲击 无断裂 ASTM D256
硬度  额定值单位制 测试方法
硬度计硬度 (邵氏 D) 40 ASTM D2240
   
注射  额定值单位制 
干燥温度  90.0 到 100°C 
干燥时间  3.0 到 4.0hr 
建议的最大水分含量 0.10% 
螺筒后部温度 190 到 210°C 
螺筒中部温度 175 到 200°C 
螺筒前部温度 165 到 180°C 
射嘴温度  190 到 210°C 
加工（熔体）温度 190 到 210°C 
模具温度  20.0 到 40.0°C