ASTALOY™ PC/ABS KMX
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

产品说明

ASTALOY™ PC/ABS KMX is a flame retardant alloy of ABS and Polycarbonate and is designed to meet the stringent Underwriter's Laboratory UL94 V-0 test whilst offering an exceptional balance of impact toughness, product rigidity, heat resistance and mouldability. Typical applications include computer casing mouldings, electrical switchgear assemblies and whitegoods clothes dryer doors.

Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS KMXU ].

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 南美洲 • 亚太地区 
添加剂 • 阻燃   
性能特点 • 抗撞击性，良好 • 耐热性，中等 • 阻燃性能 
 • 良好的成型性能 • 中等硬度  
    
用途 • 大型家用电器和小型家用电器   
UL 档案号 • E183535-C   

物理性能  额定值单位制 测试方法
比重  1.22g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 2.5g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 2 (3.20 mm) 53.0MPa ASTM D638
伸长率 2 (断裂, 3.20 mm) 60% ASTM D638
弯曲模量 3 (3.20 mm) 2400MPa ASTM D790
弯曲强度 3 (3.20 mm) 86.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 400J/m ASTM D256
落锤冲击 (3.20 mm) 45.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 114 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 98.0°C 
1.8 MPa, 未退火, 6.40 mm 105°C 
1.8 MPa, 未退火, 12.7 mm 111°C 
维卡软化温度 134°C ASTM D1525 4
线形膨胀系数 - 流动 0.000072cm/cm/°C ASTM D696
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) V-0 UL 94
热灯丝点火温度 (1.60 mm) 960°C AS/NZS 60695.2.12
   
注射  额定值单位制 
干燥温度  95.0 到 100°C 
干燥时间  3.0 到 5.0hr 
螺筒后部温度 225 到 240°C 
螺筒中部温度 230 到 245°C 
螺筒前部温度 235 到 250°C 
加工（熔体）温度 235 到 245°C 
模具温度  50.0 到 90.0°C 
注塑温度  60.0 到 140MPa 
注射速度  中等 
背压  0.100 到 0.500MPa 
螺杆转速  40 到 60rpm 
合模力  4.0 到 8.0kN/cm² 
 
ASTALOY™ PC/ABS KMX 2012年9月25日
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

备注
1 一般属性：这些不能被视为规格。

2 5.0 mm/min

3 1.3 mm/min