ASTALOY™ PC/ABS M150-28328
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

产品说明

ASTALOY™ PC/ABS M150-28328 is highly pigmented, ultra high heat resistance and ultra high impact strength alloy of Polycarbonate/ABS and is designed for moulding applications requiring reduced light bleed and exceptional impact toughness, product rigidity, ultra high heat resistance whilst maintaining mouldability. Typical applications include light box display units

Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS M150U-28328 ].

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 南美洲 • 亚太地区 
性能特点 • 超高抗冲击性 • 良好的成型性能  
 • 刚性，良好 • 耐热性，高  
    
用途 • Displays   
加工方法 • 注射成型   

物理性能  额定值单位制 测试方法
比重  1.33g/cm³ ASTM D792
熔流率 (250°C/3.8 kg) 7.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 2 (3.20 mm) 54.0MPa ASTM D638
伸长率 2 (断裂, 3.20 mm) 130% ASTM D638
弯曲模量 3 (3.20 mm) 2750MPa ASTM D790
弯曲强度 3 (3.20 mm) 90.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 550J/m ASTM D256
落锤冲击 (3.20 mm) 55.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 116 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 116°C 
1.8 MPa, 未退火, 6.40 mm 121°C 
1.8 MPa, 未退火, 12.7 mm 126°C 
维卡软化温度 150°C ASTM D1525 4
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
灼热丝易燃指数 (3.20 mm) 750°C AS/NZS 60695.2.12
   
注射  额定值单位制 
干燥温度  95.0 到 100°C 
干燥时间  3.0 到 5.0hr 
螺筒后部温度 245 到 265°C 
螺筒中部温度 255 到 275°C 
螺筒前部温度 265 到 285°C 
加工（熔体）温度 260 到 290°C 
模具温度  50.0 到 90.0°C 
注塑温度  60.0 到 140MPa 
注射速度  中等 
背压  0.100 到 0.500MPa 
螺杆转速  40 到 60rpm 
合模力  4.0 到 8.0kN/cm² 
 
ASTALOY™ PC/ABS M150-28328 2012年9月25日
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

备注
1 一般属性：这些不能被视为规格。

2 5.0 mm/min

3 1.3 mm/min

压 力1 (10N)