ASTALOY™ PC/ABS MT7228HF
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

产品说明

ASTALOY™ PC/ABS MT7228HF is a high melt flow, high heat resistance and high impact strength alloy of Polycarbonate & ABS which has been designed for injection moulding applications requiring a balance of exceptional impact toughness (especially at low temperatures), high product rigidity and a high heat resistance whilst maintaining easy processing and ease of decorative painting.

Note: The last letter U indicates additional UV stabilisation has been added [ ie: ASTALOY™ PC/ABS MT7228HFU].

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 南美洲 • 亚太地区 
 • 刚性，高 • 流动性高 • 适于粉刷 
性能特点 • 抗撞击性，高 • 耐低温撞击  
 • 可加工性，良好 • 耐热性，高  
加工方法 • 注射成型   

物理性能  额定值单位制 测试方法
比重  1.14g/cm³ ASTM D792
熔流率   ASTM D1238
250°C/3.8 kg 10g/10 min 
260°C/5.0 kg 24g/10 min 
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.10% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 2 (3.20 mm) 56.0MPa ASTM D638
伸长率 2 (断裂, 3.20 mm) 150% ASTM D638
弯曲模量 3 (3.20 mm) 2450MPa ASTM D790
弯曲强度 3 (3.20 mm) 92.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.50 mm) 680J/m ASTM D256
落锤冲击 (3.50 mm) 65.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 116 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 112°C 
1.8 MPa, 未退火, 6.40 mm 117°C 
1.8 MPa, 未退火, 12.7 mm 122°C 
维卡软化温度 143°C ASTM D1525 4
线形膨胀系数 - 流动 0.000070cm/cm/°C ASTM D696
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
灼热丝易燃指数 (1.60 mm)a
注射速度  中等 
背压  0.100 到 0.500MPa 
螺杆转速  40 到 60rpm 
 
ASTALOY™ PC/ABS MT7228HF 2012年9月25日
丙烯腈丁二烯苯乙烯+聚碳酸酯 
Marplex Australia Pty. Ltd. 
注射 额定值单位制
合模力 4.0 到 8.0kN/cm²

备注
1 一般属性：这些不能被视为规格。

2 5.0 mm/min

3 1.3 mm/min

4 压 力1 (10N)