ASTALOY™ PC/ABS TWG
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

产品说明

ASTALOY™ TWG is a high weldline impact strength alloy of ABS and Polycarbonate and is designed for injection moulding applications with multiple weldlines and requiring a balance of impact toughness, heat resistance, product rigidity, mouldability and easy painting. Typical applications in the automotive area are interior instrument panel fascia panels, console capping mouldings and glovebox assemblies, together with exterior painted components such as wheeltrims, front grilles, rear appliques and other trim panels.

Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ TWG-U ].

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 南美洲 • 亚太地区 
性能特点 • 抗撞击性，高 • 耐热性，高 • 中等硬度 
 • 良好的成型性能 • 适于粉刷  
    
用途 • 汽车领域的应用： • 汽车内部零件 • 汽车外部零件 
加工方法 • 注射成型   

物理性能  额定值单位制 测试方法
比重  1.12g/cm³ ASTM D792
熔流率 (250°C/3.8 kg) 8.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 2 (3.20 mm) 53.0MPa ASTM D638
伸长率 2 (断裂, 3.20 mm) 100% ASTM D638
弯曲模量 3 (3.20 mm) 2400MPa ASTM D790
弯曲强度 3 (3.20 mm) 85.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 600J/m ASTM D256
落锤冲击 (3.20 mm) 60.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 112 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 102°C 
1.8 MPa, 未退火, 6.40 mm 107°C 
1.8 MPa, 未退火, 12.7 mm 112°C 
维卡软化温度 135°C ASTM D1525 4
线形膨胀系数 - 流动 0.000072cm/cm/°C ASTM D696
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695.2.12
   
注射  额定值单位制 
干燥温度  95.0 到 100°C 
干燥时间  3.0 到 5.0hr 
螺筒后部温度 235 到 255°C 
螺筒中部温度 245 到 265°C 
螺筒前部温度 255 到 275°C 
加工（熔体）温度 250 到 280°C 
模具温度  50.0 到 90.0°C 
注塑温度  60.0 到 140MPa 
注射速度  中等 
背压  0.100 到 0.500MPa 
螺杆转速  40 到 60rpm 
合模力  4.0 到 8.0kN/cm² 
 
ASTALOY™ PC/ABS TWG 2012年9月25日
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

备注
1 一般属性：这些不能被视为规格。

2 5.0 mm/min

3 1.3 mm/min

4 压 力1 (10N)