CABELEC® CA6141
聚碳酸酯
Cabot Corporation 

Technical Data

产品说明

CABELEC® 6141 is an electrically conductive compound based on conductive carbon black dispersed in a modified polycarbonate. CABELEC® 6141 has been specially formulated for injection moulding applications. It has been developed to give a balanced property profile with permanent electrical conductivity.

CABELEC® 6141 is recommended for packaging and electronic product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosive powders, pigments and electronic components.

总体

材料状态 • 已商用：当前有效  
资料 1 •  Technical Datasheet (English)
 
  •  Processing - Cablelec (English)
 
    
供货地区 • 北美洲 • 欧洲 
 • 南美洲 • 亚太地区 
    
添加剂 • 碳黑  
性能特点 • 导电  
用途  • 包装 • 电气/电子应用领域 
机构评级 • EC 1907/2006 (REACH)  
外观  • 黑色  
形式  • 颗粒料  
加工方法 • 注射成型  

 物理性能  额定值单位制 测试方法
 密度 3  1.20g/cm³ Internal Method
 熔流率 4   ISO 1133
 260°C/10.0 kg 12g/10 min 
 260°C/2.16 kg 0.60g/10 min 
 260°C/5.0 kg 4.0g/10 min 
 收缩率 - 流动 5 0.70 到 0.90% ASTM D955
 机械性能  额定值单位制 测试方法
 拉伸应力 6  ISO 527-2
 屈服  54.0MPa 
 断裂  47.0MPa 
 拉伸应变 6 (断裂) 24% ISO 527-2
 弯曲模量 7 2170MPa ISO 178
 冲击性能  额定值单位制 测试方法
 悬壁梁缺口冲击强度 8 (23°C) 22kJ/m² ISO 180
 硬度  额定值单位制 测试方法
 硬度计硬度 9 (邵氏 D, 15 秒) 80 ASTM D2240
 热性能  额定值单位制 测试方法
 热变形温度 10 (1.8 MPa, 未退火) 121°C ISO 75-2/A
 维卡软化温度 11 149°C ISO 306/A
 电气性能  额定值单位制 测试方法
 表面电阻率 12 1.0E+5ohm Internal Method
 体积电阻率 13 2.0E+2ohm•cm Internal Method
    
 注射  额定值单位制 
 干燥温度  100°C 
 干燥时间  2.0 到 4.0hr 
 螺筒中部温度 270°C 
 射嘴温度  290°C 
1 / 3   
 
CABELEC® CA6141
聚碳酸酯
Cabot Corporation  
     
  注射 额定值单位制 
    
  模具温度 80.0°C 

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 CTM E023

4 CTM E005

5 CTM E047

6 CTM E041

7 CTM E040A

8 CTM E044A

9 CTM E030

10 CTM E038

11 CTM E039

12 CTM E042E

13 CTM E043B