ASTALON™ H2000R
聚碳酸酯
Marplex Australia Pty. Ltd.
Technical Data
产品说明
ASTALON™ H2000R / H2001R / H2003R are low/medium viscosity (high melt flow) grades in the ASTALON™ range and are well suited to difficult to fill injection moulding applications which require a mould release agent (R). Offering an excellent balance of transparency, toughness, heat resistance, flame retardancy and processability, typical applications include security cases and point of sale displays. Note: [ Standard grade = H2000R ] / [ FDA approved = H2001R ] / [ Steam resistant = H2003R ].
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
Search for UL Yellow Card • Marplex Australia Pty. Ltd.
供货地区 • 北美洲 • 南美洲 • 亚太地区
添加剂 • 脱模
• 可加工性，良好 • 韧性良好 • 阻燃性能
性能特点 • 流动性高 • 中等透明度
• 耐热性，中等 • 中等粘性
用途 • Displays
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.20g/cm³ ASTM D792
熔流率 (300°C/1.2 kg) 22g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.24% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 61.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 120% ASTM D638
弯曲模量 4 (6.40 mm) 2350MPa ASTM D790
弯曲强度 4 (6.40 mm) 88.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 580J/m ASTM D256
落锤冲击 (3.20 mm) 75.0J ASTM D3029
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 122 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
0.45 MPa, 未退火, 6.40 mm 141°C
1.8 MPa, 未退火, 6.40 mm 131°C
线形膨胀系数 - 流动 0.000060 到 0.000070cm/cm/°C ASTM D696
电气性能 额定值单位制 测试方法
体积电阻率 2.1E+16ohm•cm ASTM D257
介电常数 2.85 ASTM D150
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) V-2 UL 94
光学性能 额定值单位制 测试方法
透射率 (总计, 3000 µm) 85.0% ASTM D1003
注射 额定值单位制
干燥温度 120 到 125°C
干燥时间 4.0 到 6.0hr
螺筒后部温度 230 到 245°C
螺筒中部温度 240 到 255°C
1 / 3
ASTALON™ H2000R
聚碳酸酯
Marplex Australia Pty. Ltd.
注射 额定值单位制
螺筒前部温度 250 到 265°C
加工（熔体）温度 240 到 270°C
模具温度 60.0 到 110°C
注塑温度 60.0 到 140MPa
注射速度 中等
背压 0.100 到 0.500MPa
螺杆转速 40 到 60rpm
合模力 4.0 到 8.0kN/cm²
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2 一般属性：这些不能被视为规格。
3 20 mm/min
4 2.8 mm/min
|