ULTEM* CRS5311 Resin
聚醚酰亚胺
SABIC Innovative Plastics
Technical Data
产品说明
30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet
UL Yellow Card 2 • E121562-221121
Search for UL Yellow Card • SABIC Innovative Plastics
• ULTEM*
供货地区 • 北美洲
填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量
性能特点 • 符合 ECO • 耐化学性良好 • 耐酸
• 共聚物 • 耐碱
机构评级
加工方法
多点数据
• EU Eco
• 注射成型
• Elastic Modulus vs • Instrumented Impact (Load) • Tensile Stress vs. Strain (ASTM
Temperature (ASTM D4065) (ASTM D3763) D638)
• • • Thermal Conductivity vs.
Flexural DMA (ASTM D4065) Specific Heat vs. Temperature
• Instrumented Impact (Energy) (ASTM D3417) Temperature (ASTM E1530)
• Viscosity vs. Shear Rate
(ASTM D3763) • Tensile Fatigue
(ASTM D3835)
物理性能 额定值单位制 测试方法
比重 1.52g/cm³ ASTM D792
熔流率 (337°C/6.6 kg) 4.0g/10 min ASTM D1238
收缩率 - 流动 (3.20 mm) 0.20 到 0.40% Internal Method
机械性能 额定值单位制 测试方法
拉伸模量 4 8960MPa ASTM D638
抗张强度 5 (断裂) 165MPa ASTM D638
伸长率 5 (断裂) 3.0% ASTM D638
弯曲模量 6 (100 mm 跨距) 8960MPa ASTM D790
弯曲强度 6 (屈服, 100 mm 跨距) 234MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 ASTM D256
Natural, Tints 160J/m
23°C 96J/m
反向缺口冲击 (3.20 mm) 510J/m ASTM D256
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火, 6.40 mm) 219°C ASTM D648
RTI Elec 105°C UL 746
RTI Imp 105°C UL 746
RTI Str 105°C UL 746
电气性能 额定值单位制 测试方法
耐电弧性 7 PLC 5 ASTM D495
相比耐漏电起痕指数(CTI) PLC 4 UL 746
高电弧燃烧指数(HAI) PLC 4 UL 746
高电压电弧起痕速率 (HVTR) PLC 3 UL 746
热丝引燃 (HWI) PLC 0 UL 746
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.47 mm) • V-0 UL 94
• 5VA
ULTEM* CRS5311 Resin
聚醚酰亚胺
SABIC Innovative Plastics
注射 额定值单位制
干燥温度 149°C
干燥时间 4.0 到 6.0hr
干燥时间，最大 24hr
建议的最大水分含量 0.020%
建议注入量 40 到 60%
螺筒后部温度 343 到 366°C
螺筒中部温度 354 到 377°C
螺筒前部温度 366 到 388°C
射嘴温度 360 到 382°C
加工（熔体）温度 366 到 388°C
模具温度 135 到 163°C
背压 0.345 到 0.689MPa
螺杆转速 40 到 70rpm
排气孔深度 0.025 到 0.076mm
|